Degradation in the fatigue strength of dentin by cutting, etching and adhesive bonding

H H Lee; H Majd; S Orrego; B Majd; E Romberg; M M Mutluay; D Arola

doi:10.1016/j.dental.2014.06.005

Degradation in the fatigue strength of dentin by cutting, etching and adhesive bonding

Dent Mater. 2014 Sep;30(9):1061-72. doi: 10.1016/j.dental.2014.06.005. Epub 2014 Jun 28.

Authors

H H Lee¹, H Majd², S Orrego², B Majd², E Romberg³, M M Mutluay⁴, D Arola⁵

Affiliations

¹ Department of Biomaterials Science, College of Dentistry, Dankook University, Republic of Korea; Institute of Tissue Regeneration Engineering, Dankook University, Republic of Korea.
² Department of Mechanical Engineering, University of Maryland Baltimore County, Baltimore, MD, USA.
³ Department of Orthodontics, Dental School, University of Maryland, Baltimore, MD, USA.
⁴ Department of Mechanical Engineering, University of Maryland Baltimore County, Baltimore, MD, USA; Adhesive Dentistry Research Group, Department of Cariology, Institute of Dentistry, University of Turku, Turku, Finland.
⁵ Department of Materials Science and Engineering, University of Washington, Seattle, WA USA; Department of Restorative Dentistry, School of Dentistry, University of Washington, Seattle, WA USA. Electronic address: darola@uw.edu.

Abstract

The processes involved in placing resin composite restorations may degrade the fatigue strength of dentin and increase the likelihood of fractures in restored teeth.

Objective: The objective of this study was to evaluate the relative changes in strength and fatigue behavior of dentin caused by bur preparation, etching and resin bonding procedures using a 3-step system.

Methods: Specimens of dentin were prepared from the crowns of unrestored 3rd molars and subjected to either quasi-static or cyclic flexural loading to failure. Four treated groups were prepared including dentin beams subjected to a bur treatment only with a conventional straight-sided bur, or etching treatment only. An additional treated group received both bur and etching treatments, and the last was treated by bur treatment and etching, followed by application of a commercial resin adhesive. The control group consisted of "as sectioned" dentin specimens.

Results: Under quasi-static loading to failure there was no significant difference between the strength of the control group and treated groups. Dentin beams receiving only etching or bur cutting treatments exhibited fatigue strengths that were significantly lower (p≤0.0001) than the control; there was no significant difference in the fatigue resistance of these two groups. Similarly, the dentin receiving bur and etching treatments exhibited significantly lower (p≤0.0001) fatigue strength than that of the control, regardless of whether an adhesive was applied.

Significance: The individual steps involved in the placement of bonded resin composite restorations significantly decrease the fatigue strength of dentin, and application of a bonding agent does not increase the fatigue strength of dentin.

Keywords: Adhesive resin; Bonding; Dentin; Etching; Fatigue; Tooth fracture.

Publication types

Research Support, N.I.H., Extramural
Research Support, Non-U.S. Gov't

MeSH terms

Acid Etching, Dental*
Dental Bonding*
Dental Stress Analysis
Dentin*
Humans
In Vitro Techniques

Abstract