The synthesis of metal-organic frameworks with large three-dimensional channels that are permanently porous and chemically stable offers new opportunities in areas such as catalysis and separation. Two linkers (L1=4,4',4'',4'''-([1,1'-biphenyl]-3,3',5,5'-tetrayltetrakis(ethyne-2,1-diyl)) tetrabenzoic acid, L2=4,4',4'',4'''-(pyrene-1,3,6,8-tetrayltetrakis(ethyne-2,1-diyl))tetrabenzoic acid) were used that have equivalent connectivity and dimensions but quite distinct torsional flexibility. With these, a solid solution material, [Zr6 O4 (OH)4 (L1)2.6 (L2)0.4 ]⋅(solvent)x , was formed that has three-dimensional crystalline permanent porosity with a surface area of over 4000 m(2) g(-1) that persists after immersion in water. These properties are not accessible for the isostructural phases made from the separate single linkers.
Keywords: mesoporous materials; metal-organic frameworks; water stability; zirconium.
© 2014 The Authors. Published by Wiley-VCH Verlag GmbH & Co. KGaA. This is an open access article under the terms of the Creative Commons Attribution License, which permits use, distribution and reproduction in any medium, provided the original work is properly cited.