Conducting polymer (CP) thin films find widespread use, for example in bioelectronic, energy harvesting and storage, and drug delivery technology. Electrosynthesis at a polarizable liquid|liquid interface using an aqueous oxidant and organic soluble monomer provides a route to free-standing and scalable CP thin films, such as poly(3,4-ethylenedioxythiophene) (PEDOT), in a single step at ambient conditions. Here, using the potentiodynamic technique of cyclic voltammetry, interfacial electrosynthesis involving ion exchange, electron transfer, and proton adsorption charge transfer processes is shown to be mechanistically distinct from CP electropolymerization at a solid electrode|electrolyte interface. During interfacial electrosynthesis, the applied interfacial Galvani potential difference controls the interfacial concentration of the oxidant, but not the CP redox state. Nevertheless, typical CP electropolymerization electrochemical behaviors, such as steady charge accumulation with each successive cycle and the appearance of a nucleation loop, were observed. By combining (spectro)electrochemical measurements and theoretical models, this work identifies the underlying mechanistic origin of each feature on the cyclic voltammograms (CVs) due to charge accumulated from Faradaic and capacitive processes as the PEDOT thin film grows. To prevent overoxidation during interfacial electrosynthesis with a powerful cerium aqueous oxidant, scan rates in excess 25 mV·s-1 were optimal. The experimental methodology and theoretical models outlined in this article provide a broadly generic framework to understand evolving CVs during interfacial electrosynthesis using any suitable oxidant/monomer combination.