Porous nitrogen-doped graphene (PNG) materials with high conductivity, high surface area, and chemical stability have displayed superior performance in electrochemical capacitors. However, previously reported methods for fabricating PNG render the processes expensive, hard to control, limited in production, and unsafe as well, thus largely restricting their practical applications. Herein, we present a facile two-step calcination method to prepare PNG using petroleum asphalt as the carbon source to provide the original three-dimensional porous structure directly and using environmentally friendly and high nitrogen content urea as the nitrogen source without adding any etching agent. The porous structure in PNG can largely increase its specific surface area, and the introduction of nitrogen atoms can effectively increase the degree of defects and improve the wettability of PNG. As a result, PNG displays a high specific capacitance of 157 F g-1 at a current density of 1 A g-1 and cycling stability while maintaining 98.68% initial capacitance after 10,000 cycles.
Keywords: electrochemical capacitors; petroleum asphalt; porous nitrogen-doped graphene.