The absence of carbon fiber-reinforced rebar performance standards in Korea has limited its reliability. This study investigates the durability performance of carbon fiber-reinforced polymer rebar as an alternative to traditional steel reinforcement in concrete structures. Concrete beams reinforced with carbon fiber-reinforced polymer rebar were exposed to chloride environments for durations of 35 and 70 days and then subjected to bending tests to evaluate their durability. The results demonstrate that the strong bond between the carbon fiber-reinforced polymer and concrete effectively prevented brittle fracture, even under exposure to harsh chloride. A scanning electron microscope analysis of the specimens exposed to chloride showed no deterioration of the carbon fiber-reinforced polymer rebar, highlighting its exceptional resistance to corrosion. Furthermore, durability tests were conducted in a carbonation chamber for 8 and 12 weeks, with no signs of degradation in the carbon fiber-reinforced polymer rebar. These findings suggest that carbon fiber-reinforced polymer rebar offers excellent resistance to both chloride-induced corrosion and carbonation, making it a promising solution to enhance the longevity and durability of reinforced concrete structures exposed to aggressive environmental conditions.
Keywords: carbon fiber-reinforced polymer; carbonation test; chloride environment; durability test; exposure experiment.