This paper introduces cross-wound CFRP shear reinforcement of hollow HPC beams. The CFRP reinforcement was manufactured in the form of a square tubular mesh from carbon rovings oriented at ±45° from the longitudinal axis. The shear reinforcement was made in two variants from carbon yarns with linear densities of 1600 and 3700 tex. Tensile reinforcement made of BFRP bars was positioned directly around the hollow core and was used as a platform for manual winding of the shear reinforcement. The hollow beams were subjected to a three-point bending test with four configurations of the tensile BFRP reinforcement for better evaluation of the effect of the shear reinforcement under different conditions. The 1600 tex shear reinforcement increased the ultimate flexural strength by at least 89% compared to specimens without any shear reinforcement. The 3700 tex shear reinforcement yielded slightly better results in most cases but was not utilized to its full shear capacity as these specimens always failed in shear due to the delamination of the concrete matrix from the shear reinforcement. There was too much reinforcement in the beam cross-section.
Keywords: composite reinforcement; cross-wound reinforcement; fiber-reinforced polymer; high-performance concrete; hollow concrete beam; shear reinforcement; woven reinforcement.